Method for Producing Nano-Particles of Molybdenum Oxide

ABSTRACT

Method for producing nano-particles includes vaporizing a precursor material to produce a vapor, directing the vapor into an isolation chamber, combining a quench fluid in a gaseous state with a quench fluid in a liquid state to form a quench fluid stream, contacting the vapor contained in the isolation chamber with the quench fluid stream thereby cooling the vapor to produce the nano-particles in a carrier stream, and removing the nano-particles from the isolation chamber.

CROSS-REFERENCE TO RELATED APPLICATION

This is a continuation of U.S. patent application Ser. No. 10/438,597, filed May 15, 2003, which is a continuation-in-part of U.S. patent application Ser. No. 10/222,626 filed Aug. 16, 2002, which is a divisional of U.S. patent application Ser. No. 09/709,838, filed on Nov. 9, 2000, now U.S. Pat. No. 6,468,497 B1, all of which are incorporated herein by reference for all that they disclose.

FIELD OF INVENTION

This invention relates to the production of nano-particles in general and more particularly to a method and apparatus for producing nano-particles of molybdenum oxide.

BACKGROUND

Nano-particles, that is, particles having average sizes less than about 1 micrometer (i.e., 1 micron) are known in the art and are of interest because their nano-crystalline and/or other nano-scale features dramatically change the properties of the material. For example, certain materials fabricated from nano-particles often possess superior mechanical properties compared with the same material fabricated in a conventional manner and with conventionally-sized starting materials (e.g., powders). Nano-particles of other materials may also possess unique electrical and/or magnetic properties, thereby opening the door to the fabrication of materials having previously unforeseen properties and attributes. The extremely large surface area to weight ratio of nano-particles allows nano-particles to interact with their surroundings very quickly which can also lead to the fabrication of new materials having new properties.

In sum, it is recognized that the ability to produce any material in nano-particle form represents a unique opportunity to design and develop a wide range of new and useful mechanical, optical, electrical, and chemical applications, just to name a few. However, one problem that heretofore has limited the use of nano-particles is the difficulty in producing nano-particles of the desired size and composition on a commercial scale, e.g., by the kilogram instead of by the gram.

One method for producing nano-particles involves dissolving in a solvent precursor chemicals which define the composition of the final nano-particle product. The resulting composition is mixed to yield a solution which is substantially homogenous on a molecular level. The solvent is then evaporated at a sufficient rate so that the components in the homogenized solution are precipitated as a homogenized solid powder. While such wet processes have been used to produce nano-particles of various compositions, they are not without their problems. For example, such processes tend to produce larger particles along with the nano-particles, which must then be removed or separated from the nano-particles before the nano-particles can be used. Such wet processes can also involve a significant number of process steps and reagents which tend to increase the overall cost of the final nano-particle product.

Another method for producing nano-particles is a primarily mechanical process in which the precursor material is ground in a mill (e.g., a ball mill) until particles of the desired size are produced. Unfortunately, however, such grinding processes are energy intensive, require substantial amounts of time, and typically result in the production of a powder containing not only the desired nano-particle product, but also particles having larger sizes as well. Of course, such larger sized particles must be separated from the nano-particles before they can be used. The abrasive materials used in such milling and grinding processes also tend to contaminate the nano-particle material. Consequently, such grinding processes generally are not conducive to the production of a highly pure nano-particle product.

Several other processes have been developed in which the precursor material is vaporized, typically in a partial vacuum, and then rapidly cooled in order to initiate nucleation and precipitate the nano-particle material. For example, in one process, a stream of vaporized precursor material is directed onto the surface of a cold (i.e., refrigerated) rotating cylinder. The vapor condenses on the cold surface of the cylinder. A scraper placed in contact with the rotating cylinder scrapes off the condensed material, which is then collected as the nano-particle product. In another process, the vapor stream of precursor material is condensed by expanding the vapor stream in a sonic nozzle. That is, the vapor stream is initially accelerated in the converging portion of the nozzle, ultimately reaching sonic velocity in the throat of the nozzle. The vapor stream is then further accelerated to a supersonic velocity in the diverging section of the nozzle. The supersonic expansion of the vapor stream rapidly cools the vapor stream which results in the precipitation of nano-sized particles.

While the foregoing vaporization and cooling processes have been used to produce nano-particle materials, they are not without their problems. For example, the rotating cold cylinder process has proved difficult to implement on a large scale basis and has been less than successful in producing large quantities of nano-particle material. While the sonic nozzle process is theoretically capable of producing large quantities of nano-particles on a continuous basis, it requires the maintenance of a proper pressure differential across the sonic nozzle throughout the process. Another problem with the sonic nozzle process is that the nano-particle material tends to condense on the nozzle walls, which can seriously reduce the efficiency of the nozzle, and may even prevent it from functioning. While the condensation problem can be reduced by injecting a boundary layer stream along the nozzle walls, such a provision adds to the overall complexity and operational cost of the system.

Consequently, a need remains for a method and apparatus for producing nano-particles that does not suffer from the shortcomings of the prior art methods. Such a method and apparatus should be capable of producing large quantities of nano-particle product, preferably on a continuous basis, and at a low cost. Ideally, such a method and apparatus should be less sensitive to certain process parameters than other systems, thereby allowing the method and apparatus to be more easily practiced on a large scale (i.e., commercial) basis. Additional advantages could be realized if the method and apparatus produced nano-particles in a relatively narrow size range, with a minimum amount of larger sized particles and/or contaminant materials.

SUMMARY OF THE INVENTION

A method for producing nano-particles from a precursor material may comprise the steps of: vaporizing the precursor material to produce a vapor; directing the vapor into an isolation chamber; combining a quench fluid in a gaseous state with a quench fluid in a liquid state to form a quench fluid stream; contacting the vapor contained in the isolation chamber with the quench fluid stream to precipitate nano-particles in a carrier stream; and removing the nano-particles from the isolation chamber.

In another embodiment, the method for producing nano-particles may comprise providing a supply of precursor material; providing a supply of quench fluid; separating the supply of quench fluid into a first quench fluid supply and a second quench fluid supply, the first quench fluid supply and the second quench fluid supply consisting essentially of the same substance, the first quench fluid supply being the quench fluid in the gaseous state and the second quench fluid supply being the quench fluid in the liquid state; sublimating the precursor material to produce vapor; directing the vapor into an isolation chamber; creating a quench fluid stream by withdrawing quench fluid in the gaseous state from the first quench fluid supply, withdrawing quench fluid in the liquid state from the second quench fluid supply and combining the quench fluid in the gaseous state with the quench fluid in the liquid state; directing the quench fluid stream into the isolation chamber; contacting the vapor in the isolation chamber with the quench fluid stream, producing nano-particles; and removing the nano-particles from the isolation chamber.

BRIEF DESCRIPTION OF THE DRAWING

Illustrative and presently preferred embodiments of the invention are shown in the accompanying drawing in which:

FIG. 1 is a schematic representation of the apparatus for producing nano-particles according to one embodiment of the invention;

FIG. 2 is a cross-sectional view in elevation of the precipitation conduit in which the nano-particles are formed;

FIG. 3 is a cross-sectional view in elevation of the product collection manifold;

FIG. 4 is a transmission electron microscope image of an MoO₃ nano-particle product produced by the present invention;

FIG. 5 is schematic representation of the apparatus for producing nano-particles according to another embodiment of the invention; and

FIG. 6 is a transmission electron microscope image of an MoO₃ nano-particle produced by the embodiment of the invention illustrated in FIG. 5.

DETAILED DESCRIPTION OF THE INVENTION

Apparatus 10 for producing nano-particles of a precursor material is shown and described herein as it may be used to produce nano-particles 12 (FIGS. 2-4) of molybdenum oxide (MoO₃) from a precursor material 14. Alternatively, the apparatus 10 may be used to produce nano-particles of other vaporizable or sublimable materials, as will be described in greater detail below. In the embodiment shown and described herein, the apparatus 10 for producing nano-particles 12 may comprise a sublimation furnace 16 having at least one vapor region 18 associated therewith. A precipitation conduit 20 having an inlet end 22 and an outlet end 24 extends into the vapor region 18 so that the inlet end 22 of precipitation conduit 20 is exposed to vaporized (e.g., sublimated) material 36 contained within the vapor region 18. The outlet end 24 of conduit 20 is connected to a product collection apparatus 26 which collects the nano-particle product 12.

The inlet end 22 of precipitation conduit 20 is best seen in FIG. 2 and defines an isolation chamber 28 within which is provided a quench fluid port 30. The quench fluid port 30 is connected to a supply of a quench fluid 32, such as liquid nitrogen. See FIG. 1. The quench fluid 32 is discharged from the quench fluid port 30 as a fluid stream 34. As will be described in greater detail below, the fluid stream 34 rapidly cools the vaporized material 36 flowing through the precipitation conduit 20. This rapid cooling results in the precipitation of the nano-particle material 12 within the precipitation conduit 20. The precipitated nano-particle material 12 continues to be carried along the precipitation conduit 20 to the product collection apparatus 26.

The product collection apparatus 26 may comprise a filter assembly 40 and a pump assembly 42 that is fluidically connected to the filter assembly 40. The pump assembly 42 draws or pumps the vaporized material 36 from the vapor region 18, into the precipitation conduit 20, and ultimately through the filter assembly 40. More specifically, the vaporized material 36 is converted within the precipitation conduit 20 into a carrier stream having the nano-particle material 12 suspended therein. The carrier stream containing the suspended nano-particle material 12 continues to be drawn through the precipitation conduit 20 under the action of pump 42, ultimately reaching the filter assembly 40. The filter assembly 40 removes the nano-particle material 12 from the carrier stream. The carrier stream is then discharged into the surrounding atmosphere as filtered carrier stream 68.

The apparatus 10 for producing nano-particles may be operated as follows to produce nano-particles of molybdic oxide (MoO₃). As a first step in the process, a suitable MoO₃ precursor material 14, such as MoO₂ or MoO₃, is fed into the sublimation furnace 16. The MoO₃ precursor material 14 is sublimed (i.e., converted directly to a vapor or gas state from a solid state without passing through a liquid state) within the sublimation furnace 16, resulting in the production of a sublimed or vapor state material 36. The sublimed or vapor state material 36 is generally contained within the vapor region 18. Depending on the composition of the precursor material 14, the sublimed (i.e., vaporized) material 36 may be combined with a suitable oxygen-containing carrier gas 38 (e.g, air) in order to fully oxidize the sublimed material. The carrier gas 38 may be allowed to enter the vapor region 18 through a suitable opening 70 provided therein. Such additional oxidation may be required or desired if the precursor material comprises “sub-oxide” material (e.g, MoO₂) and where the nano-particle material 12 is to be MoO₃.

Once the pump 42 of the product collection apparatus 26 is activated, it draws the sublimed or vaporized material 36 contained within the vapor region 18 into the inlet end 22 of precipitation conduit 20. The sublimed material 36 first enters the isolation chamber 28 (FIG. 2) which isolates the sublimed material from the vapor region 18. As the sublimated material 36 continues to flow through the conduit 20, the sublimed material 36 contacts and mixes with the quench fluid stream 34 emerging from the quench fluid port 30. The fluid stream 34 rapidly cools or quenches the sublimated material 36 (i.e., substantially adiabatically) which causes the precipitation of the nano-particle material 12. The precipitated nano-particle material 12 is generally suspended within a carrier stream (which may comprise air and/or other gaseous components remaining in the vapor stream 36 after the precipitation of the nano-particle material 12). Thereafter, the carrier stream containing the precipitated nano-particle material 12 continues to be carried along the conduit 20, whereupon it is ultimately collected by the filter 40 in the product collection apparatus 26. The filter 40 may be harvested from time to time to remove the accumulated nano-particle material 12.

The nano-particle material 12 of MoO₃ produced according to the method and apparatus of the present invention may be imaged in accordance with any of a wide range of microscopy processes that are now known in the art or that may be developed in the future that are suitable for imaging particles in the nano-size range. For example, FIG. 4 is an image of the nano-particle material 12 produced by a transmission electron microscope in a process generically referred to as transmission electron microscopy (TEM). As is readily seen in the TEM image illustrated in FIG. 4, each individual particle of the nano-particle material 12 comprises a generally cylindrically shaped, rod-like configuration having a mean length that is greater than the mean diameter. While the size of the nano-particle material 12 can be expressed in terms of the mean length or the mean diameter of the particles (e.g., as imaged by transmission electron microscopy), it is generally more useful to express the size of the nano-particle material 12 in terms of surface area per unit weight. Measurements of particle surface area per unit weight may be obtained by BET analysis. As is well-known, BET analysis involves an extension of the Langmiur isotherm equation using multi-molecular layer absorption developed by Brunauer, Emmett, and Teller. BET analysis is an established analytical technique that provides highly accurate and definitive results. In the embodiment shown and described herein, the method and apparatus of the present invention has produced nano-particle material having sizes in the range of about 4-44 square meters/gram (m²/g) (15-35 m²/g preferred) as measured in accordance with BET analysis. Alternatively, other types of measuring processes may be used to determine the particle size.

A significant advantage of the present invention is that it can be used to produce nano-particles of MoO₃ in very large quantities and at a very low cost. The present invention is also relatively simple to construct, easy to operate, and is not overly sensitive to certain process parameters. Consequently, the present invention is ideally suited for use in large-scale (i.e., commercial) applications. The nano-particle material 12 produced by the present invention also contains particles within a fairly narrowly defined size range and with a minimum amount of larger-sized particles. Consequently, the nano-particle material 12 produced in accordance with the method and apparatus of the present invention may be generally regarded as a high quality product that requires little or no additional processing before it may be used.

Another advantage of the present invention is that it is generally immune to problems associated with the condensation of the nano-particle material on the internal components of the precipitation conduit 20. Consequently it is not necessary to take additional measures (e.g., the injection of an insulating boundary layer) to discourage the accumulation of nano-particle material on the internal components of the system. Moreover, even if the nano-particle product eventually accumulates on the internal components of the system, the simple design of the system will allow any such accumulation to be easily removed.

Still yet other advantages are associated with the quench fluid tube 54. For example, the quench fluid tube 54 may be readily fabricated from commonly available tubing and does not require the provision of any converging/diverging sections. The placement of the quench fluid tube 54 within the inner pipe member 46 further simplifies construction of the nano-particle apparatus.

Having briefly described the method and apparatus according to one embodiment of the present invention, as well as some of their more significant features and advantages, the various embodiments of the method and apparatus for producing nano-particles of the present invention will now be described in detail.

Referring back now to FIG. 1, one embodiment of the apparatus 10 for producing nano-particles is shown and described herein as it may be used to produce nano-particles 12 of molybdenum tri-oxide (MoO₃). Alternatively, however, the present invention could also be used to produce nano-particles of other vaporizable or sublimable materials, as would be obvious to persons having ordinary skill in the art after having become familiar with the teachings of the present invention. The apparatus 10 may comprise a sublimation furnace 16 having a vapor region 18 associated therewith. The sublimation furnace 16 is suitable for receiving a supply of the precursor material 14. The precursor material 14 may be delivered to the furnace 16 in either a continuous manner or in batches. For example, in one preferred embodiment, the precursor material 14 is fed into the sublimation furnace 16 on a continuous basis by a screw-type conveyor system 60. Alternatively, of course, other precursor materials, vaporizing devices and/or product delivery schedules may also be used.

In the embodiment shown and described herein, the sublimation furnace 16 comprises an electrically heated furnace having one or more electric heating elements 50 provided therein for elevating the temperature in the sublimation furnace 16 to a level sufficient to sublimate the precursor material 14. As is commonly understood, the terms “sublimate” or “sublimation” refer to processes wherein a material is transformed directly from the solid state to the gas or vapor state without passing through the liquid state. Sublimation of the precursor material 14 allows for the production of a highly pure MoO₃ product.

As an aside, it should be noted that while sublimation furnaces are currently used to produce highly purified MoO₃ powder (conventionally referred to as sublimed molybdic oxide), the particles comprising the resulting powder produced by currently used sublimation processes are considerably larger than the nano-sized particles produced with the method and apparatus of the present invention.

Continuing now with the description, it should be noted that the present invention is not limited to use with sublimation furnaces, but could instead utilize any of a wide range of other furnaces that are now known in the art or that may be developed in the future that are or would be suitable for vaporizing or sublimating the precursor material 14. Examples of other types of furnaces that could be utilized with the present invention include, but are not limited to, muffle furnaces, induction furnaces, vacuum furnaces, plasma arc furnaces, tube furnaces, and arc furnaces. Consequently, the present invention should not be regarded as limited to the sublimation furnace 16 that is shown and described herein.

As will be discussed in greater detail below, the furnace 16 may be provided with one or more openings or inlets 70 therein to allow a carrier gas 38 to enter the sublimation region 18. Depending on the application, the carrier gas could comprise an oxidizing gas, a reducing gas, or an inert gas. Stated another way, the inlet 70 and the particular carrier gas 38 that is allowed therein allow the vaporization or sublimation process to occur within a controlled gas atmosphere. In the embodiment shown and described herein, the carrier gas 38 is air, so the inlet 70 may be open to the surrounding atmosphere.

With reference now to FIGS. 1 and 2, the precipitation conduit 20 is positioned within the sublimation furnace 16 so that the inlet end 22 of precipitation conduit 20 is contained generally within the vapor region 18 defined by the furnace 16. The outlet end 24 of the precipitation conduit 20 may be connected to a collection manifold 44 which is then connected to the product collection system 26. See FIG. 1. Alternatively, the outlet end 24 of precipitation conduit 20 may be connected directly to the product collection system 26.

The precipitation conduit 20 may comprise a generally elongate, pipe-like member 46 that defines the inlet end 22 and the outlet end 24 (FIG. 3) of precipitation conduit 20. The elongate, pipe-like member 46 may be supported along at least a portion of its length by a generally elongate, pipe-like outer member 48, as best seen in FIG. 1. In the embodiment shown and described herein, pipe-like outer member 48 is generally concentrically aligned with pipe-like inner member 46 and is separated a spaced distance therefrom so that an insulating space or annulus 52 is defined between the inner and outer pipe-like members 46 and 48. See FIG. 2. The insulating annulus 52 is advantageous in that it helps to keep the inner pipe-like member 46 cool, thereby discouraging the re-vaporization of the precipitated nano-particle material 12 flowing through the inner pipe 46.

The inner and outer pipe-like members 46 and 48 may be fabricated from any of a wide variety of materials (e.g., high-temperature alloys and stainless steels) suitable for the intended application. By way of example, in one preferred embodiment, the inner pipe member 46 is fabricated from a high-temperature alloy (e.g., Hastelloy® “C”) since the inlet end 22 of inner pipe 46 is exposed to the high temperatures in the vapor region 18. The outer pipe-like member 48 is fabricated from type SAE 316 stainless steel, although it could also be fabricated from other types of steel alloys.

The inner and outer pipe-like members 46 and 48 may have dimensions that are commensurate with the size (i.e., desired production capacity) of the apparatus 10 for producing nano-particles. In the embodiment shown and described herein, the inner pipe-like member 46 has an inside diameter of about 41.3 mm and a wall thickness of about 6.4 mm. The outer pipe-like member 48 may have an inside diameter of about 54 mm and a wall thickness of about 6 mm. Accordingly, the insulating space or annulus 52 will have a thickness of about 7 mm.

As was briefly described above, the inner, pipe-like member 46 is provided with a quench fluid port 30 that is suitable for discharging the quench fluid stream 34 into the inner, pipe-like member 46. See FIG. 2. In the embodiment shown and described herein, the quench fluid port 30 may comprise an elongate tube-like member or quench fluid tube 54 having an inlet end 56 and a J-shaped outlet end 58. The inlet end 56 of quench fluid tube 54 is connected to the supply of quench fluid 32, preferably via an accumulator 62. Accumulator 62 ensures that the quench fluid 32 (e.g., a cryogenic gas) supplied to the inlet end 56 of quench fluid tube 54 remains in the liquid state. The J-shaped outlet end 58 of quench fluid tube 54 defines the fluid port 30 and is positioned within the isolation chamber 28 so that the fluid port 30 is directed toward the outlet end 24 of precipitation conduit 20. Consequently, the quench fluid stream 34 discharged by the fluid port 30 is directed generally toward the outlet end 24 of precipitation conduit 20. See FIG. 3.

The location of the quench fluid port 30 within the isolation chamber 28 has some influence on the sizes of the nano-particles 12 produced by the apparatus 10 according to the present invention. For example, moving the location of the fluid port 30 closer to the inlet end 22 of precipitation conduit 20 generally results in larger nano-particles 12 being produced. Conversely, moving the location of the fluid port 30 away from the inlet end 22 generally results in smaller nano-particles 12. However, other factors can also affect the particle size. For example, smaller nano-particles can be produced even when the fluid port 30 is positioned closer to the inlet end 22 of fluid conduit 20 by increasing the flow rate of the product collection device 26. That is, higher flow rates (e.g., in liters/minute) will result in a higher velocity flow within the precipitation conduit 20. Of course, the velocity within the precipitation conduit 20 can also be changed by varying the inside diameter of the inner pipe 46. In another embodiment, the quench fluid port 30 may be positioned within the collection manifold 44. If so, the collection manifold 44 is regarded as part of the precipitation conduit. However, we have found that it is generally preferable to position the quench fluid port 30 within the precipitation conduit 20 in the manner shown and described herein.

Since the sizes of the nano-particles produced by the apparatus of the present invention are related to several structural and operational parameters of the invention, as described herein, the present invention should not be regarded as limited to any particular parameters or range of parameters for any given structural or operational configuration. For example, in the embodiment shown and described herein, the quench fluid port 30 is positioned within the isolation chamber 28 so that quench fluid port 30 is located about 16.5 cm from the inlet end 22 of precipitation conduit 20. This position, combined with the other parameters specified herein, will result in the formation of a nano-particle product substantially as described herein. However, depending on the flow rate provided by the product collection system 26, good results have also been obtained by positioning the quench fluid port 30 in the range of about 150-360 mm from the inlet end 22 of precipitation conduit 20. As mentioned above, it is also possible to position the quench fluid port 30 within the collection manifold 44, and such a positioning may be advantageous depending on the particular nano-particle product that is to be produced as well as on certain other process parameters.

The quench fluid tube 54 may be made from any of a wide range of materials (e.g., stainless steels) that would be suitable for the intended application. By way of example, the quench fluid tube 54 utilized in one embodiment of the invention is fabricated from type SAE 316 stainless steel. The size (i.e., inside diameter) of the quench fluid tube 54 may vary depending on the size (i.e., overall production capacity) of the apparatus 10. In the embodiment shown and described herein, the quench fluid tube 54 has an inside diameter of about 4 mm. Alternatively, of course, other tube sizes may be used, as would be obvious to persons having ordinary skill in the art after having become familiar with the teachings of the present invention.

While the quench fluid port 30 in one embodiment of the invention is provided by means of the J-shaped outlet end 58 of the quench fluid tube 54, other configurations are possible. For example, in another embodiment, the inner pipe 46 is provided with an integral flow channel therein that terminates in a discharge arm having a fluid outlet therein. The discharge arm may be generally radially oriented within the isolation chamber defined by the inner pipe and the fluid outlet may be positioned so that it is generally aligned with the central axis of the inner pipe. Such an arrangement allows the quench fluid to be discharged at about the center of the inner pipe.

It is generally preferred, but not required, to position a temperature sensor, such as a thermocouple (not shown) within the interior region of the precipitation conduit 20 at a location downstream of the quench fluid port 30 (i.e., between the quench fluid port 30 and the outlet end 24 of conduit 20). The output signal (not shown) from the thermocouple (also not shown) may then be monitored to maintain the temperature of the carrier stream and suspended nano-particle product 12 within a desired temperature range that is appropriate for the particular nano-particle material 12 being produced. By way of example, in one preferred embodiment, the thermocouple is positioned about 240 mm downstream of the quench fluid port 30. Alternatively, the thermocouple may be located at other positions.

The collection manifold 44 is best seen in FIG. 3 and serves as a convenient means for directing the nano-particles toward the product collection system 26 while allowing the supply of quenching fluid 32 to be directed into the quench fluid tube 54. More specifically, in the embodiment shown and described herein the collection manifold 44 defines an interior chamber 64 having an outlet end 66 that is connected to the product collection system 26. The outlet end 24 of the inner pipe 46 of precipitation conduit 20 terminates within the interior chamber 64 so that nano-particle material 12 exiting the precipitation conduit 20 is conveyed to the outlet end 66 of collection manifold 44. The outer support pipe 48 of precipitation conduit 20 may be secured to the collection manifold 44 (e.g., by welding) to allow the collection manifold 44 to be supported by the outer support pipe 48. The quench fluid tube 54 may pass through the collection manifold 44 where it is ultimately connected to the accumulator 62.

The collection manifold 44 may be fabricated from any of a wide range of materials suitable for the intended application, as would be obvious to persons having ordinary skill in the art after having become familiar with the teachings of the present invention. By way of example, in one preferred embodiment, the collection manifold 44 is fabricated from type SAE 316 stainless steel, although other mild steel alloys, ceramics, or other suitable materials may also be used.

The product collection system 26 is best seen in FIG. 1 and may comprise a blower or pump 42 and filter assembly 40. The blower or pump 42 draws the vaporized precursor material 36 through the precipitation conduit 20, the collection manifold 44, and filter assembly 40. More precisely, the vaporized material 36 is converted within the precipitation conduit 20 into a carrier stream having the nano-particle material 12 suspended therein. The carrier stream containing the suspended nano-particle material 12 continues to be drawn through the precipitation conduit 20 under the action of pump 42, ultimately reaching the filter assembly 40. The filter assembly 40 removes the nano-particle material 12 from the carrier stream. The carrier stream is then discharged into the surrounding atmosphere as filtered carrier stream 68. The filter assembly 40 may be harvested from time to time to remove the captured nano-particle material 12.

The blower or pump 42 utilized in the product collection system 26 may comprise any of a wide range of air pump devices that are well-known in the art and readily commercially available. By way of example, in one preferred embodiment, the pump 42 comprises a centrifugal blower having a capacity of about 2800 (e.g., 2831) liters per minute. Alternatively, the pump 42 may have either a larger or smaller capacity depending on the intended production capacity of the nano-particle production apparatus 10. In another embodiment, the pump 42 may be provided with a variable capacity to allow the user to vary the flow rate of the pump 42 to more easily effect certain changes in the sizes of the nano-particle material 12.

The filter assembly 40 may comprise any of a wide range devices suitable for removing small particles from an air stream. By way of example, in the embodiment shown and described herein, the filter assembly 40 comprises a particulate filter medium fabricated from Gore-Tex®. The filter material should be sufficiently fine so that it will capture substantially all of the nano-particle material 12 exiting the collection manifold 44. However, since filters for capturing such nano-sized particles are well-known in the art and could be easily provided by persons having ordinary skill in the art after having become familiar with the teachings of the present invention, the filter utilized in one preferred embodiment of the present invention will not be described in further detail herein.

In an alternative arrangement, the filter assembly 40 may comprise a liquid scrubber-type filter wherein the nano-particle material 12 is collected by bubbling the carrier stream and nano-particle material 12 through a liquid (e.g., alcohol), although other liquids may be used. The liquid captures the nano-particle material which may thereafter be removed from the liquid by conventional techniques. Still other filtering devices and processes are possible and could be used to capture and remove the nano-particle product 12 from the carrier stream, as would be obvious to persons having ordinary skill in the art after having become familiar with the teachings of the present invention. Consequently, the present invention should not be regarded as limited to the particular product collection apparatus shown and described herein.

The supply of quench fluid 32 may comprise a supply of a fluid suitable for effecting the rapid (i.e., substantially adiabatic) cooling of the vaporized precursor material 36. Toward this end, it is generally preferable that the supply of quench fluid 32 comprise a supply of a cryogenic fluid. As used herein, the term “cryogenic fluid” refers to a liquids that boil at temperatures of less than about 110 K (−163.15° C.) at atmospheric pressure. Cryogenic fluids include, but are not limited to, hydrogen, helium, nitrogen, oxygen, argon air, and methane. In the embodiment shown and described herein, the supply of quench fluid 32 comprises a supply of liquid nitrogen. In order to provide optimal quenching performance, it is generally preferable to place an accumulator 62 between the supply of quench fluid 32 and the inlet 56 of quench fluid tube 54. The accumulator 62 helps to ensure that the quench fluid enters the tube 54 as a liquid, as opposed to a liquid/gas mixture. Alternatively, a liquid/gas mixture can be used if increased flow-rates are desired and the end temperature is maintained within the appropriate range. Accordingly, the quench fluid 32 may enter the quench fluid tube 54 as either a pure liquid, a pure gas, or a mixture thereof so long as the temperature sensed by the thermocouple (not shown) positioned within the precipitation conduit 20 is maintained at the appropriate temperature for the particular nano-particle material 12.

The accumulator 62 may comprise any of a wide range of accumulators that are well-known in the art and that are readily commercially available. Consequently, the accumulator 62 that may be utilized in one preferred embodiment of the invention will not be described in greater detail herein.

The apparatus 10 may be operated in accordance with the following method in order to produce nano-particles 12 of MoO₃. The nano-particles 12 of MoO₃ are produced from a precursor material 14 that may comprise any of a wide range of molybdenum compounds and oxides that are convertible into MoO₃. For example, in one preferred embodiment, the precursor material may comprise a so-called “technical grade” molybdic oxide (MoO₃) powder having a typical size of about 200 U.S. Tyler mesh and preferably less than about 100 U.S. Tyler mesh. The technical grade molybdic oxide (MoO₃) precursor material 14 may be produced in accordance with any of a variety of processes that are well-known in the art, such as roasting processes and so-called “wet” processes. For example, the MoO₃ precursor material 14 may be produced according to the process disclosed in U.S. Pat. No. 5,804,151, entitled “Process for Autoclaving Molybdenum Disulfide” issued Sep. 8, 1998, which is hereby incorporated herein by reference for all that it discloses. Alternatively, the MoO₃ precursor material 14 may be produced according to the process disclosed in U.S. Pat. No. 5,820,844, entitled “Method for the Production of a Purified MoO₃ Composition,” issued Oct. 13, 1998, which is also incorporated herein by reference for all that it discloses. Technical grade MoO₃ powder is also readily commercially available from the Climax Molybdenum Company of Ft. Madison, Iowa, 52627 (USA), which is a subsidiary of Phelps Dodge Corporation.

Other precursor materials are available and could also be used in conjunction with the present invention, as would be obvious to persons having ordinary skill in the art after having become familiar with the teachings of the present invention. For example, in another embodiment, the precursor material 14 may be comprised entirely of molybdenum “sub-oxides” (e.g., MoO₂), or some combination of molybdenum “sub-oxides” and MoO₃. If so, the amount of molybdenum sub-oxides may be subsequently oxidized by providing an oxidizing atmosphere in the vapor region 18. The oxidizing atmosphere will oxidize any sub-oxides contained in the precursor material 36 before the same is drawn into the precipitation conduit 20. Additional oxygen for the oxidization process may be obtained from the carrier gas 38 (e.g., air) that is allowed to enter the vapor region 18 of the sublimation furnace 16 via the carrier gas inlet 70. Alternatively, a separate supply of an oxygen-containing gas may be provided to the vapor region 18 in order to provide the oxidizing atmosphere required to fully oxidize any sub-oxide compounds that may be present. Of course, the carrier gas could comprise other materials depending on the particular process. For example, the carrier gas 38 could also comprise a reducing gas or an inert gas.

Regardless of the particular precursor material 14 that is utilized (e.g., either MoO₃ or MoO₂), the precursor material 14 may be fed into the sublimation furnace 16 in either a continuous manner or in batches. In the embodiment shown and described herein, the precursor material 14 is fed into the furnace 16 in a continuous manner by a screw-type conveyer system 60. Once the precursor material 14 is delivered to the sublimation furnace 16, the sublimation furnace 16 heats the precursor material 14 to a temperature in the range of about 800°-1300° C. (with optimum results being obtained within a temperature range of about 1093°-1260° C.), which is sufficient to sublime the MoO₃ precursor material 14, resulting in the production of a vaporized or sublimed precursor material 36. As mentioned above, sublimation is a process wherein the precursor material transitions to a gaseous or vapor state directly from a solid state without passing through a liquid state. Sublimation of the precursor material 14 allows the production of a highly purified nano-particle product 12.

The sublimed or vaporized precursor material 36 may be combined with a carrier gas 38, such as air or any other desired atmosphere, to assist in the flow of the vaporized or sublimed precursor material 36 into the inlet end 22 of the precipitation conduit 20. As mentioned above, the carrier gas 38 may serve as a source of additional oxygen to oxidize any sub-oxides that may be contained in the vaporized precursor material 36. Alternatively, the carrier gas 38 may comprise an inert gas or may be supportive of reduction reactions if required or desired. The vaporized precursor material 36 (along with the carrier gas 38) is drawn into the inlet end 22 of the precipitation conduit 20 by the action of pump 42. Upon being drawn into the inlet end 22 of precipitation conduit 20, the vaporized precursor material 36 enters the isolation chamber 28. Isolation chamber 28 isolates the vaporized precursor material 36 from the vapor region 18. As the vaporized precursor material 36 continues to travel down the precipitation conduit 20, it eventually contacts the quench fluid stream 34 being discharged by the quench fluid port 30 provided on the J-shaped outlet end 58 of quench fluid tube 54. The quench fluid stream 34 being discharged by the fluid port 30 is considerably cooler than the vaporized precursor material 36. This results in the rapid (i.e., substantially adiabatic) cooling of the vaporized precursor material 36. The rapid cooling results in the precipitation of the nano-particle product 12 from the vaporized precursor material 36. The resulting mixture of precipitate (in the form of the nano-particle product 12) and carrier stream (e.g., air or inert or other gas atmosphere) continues to be carried down the precipitation conduit 20, whereupon it is discharged into the collection manifold 44. Thereafter, the nano-particle product 12 is ultimately captured by the filter 40 of the product collection system 26. The remaining carrier stream passes through the pump 42 and is discharged into the surrounding atmosphere as filtered carrier stream 68.

As mentioned above, any of a wide range of liquefied gases, preferably cryogenic gases, may be used as the quench fluid to effect the rapid cooling of the vaporized precursor material 36. In the embodiment shown and described herein, liquid nitrogen is used as the quench fluid and is provided to the inlet end 56 of quench fluid tube 54 at a pressure in the range of about 1.3-8.3 bar (5.1-7.6 bar preferred). The accumulator 62 ensures that the quench fluid (e.g., nitrogen) enters the inlet end 56 as a liquid, as opposed to a liquid/gas mix or in a gaseous form.

FIG. 4 is an image of the nano-particle material 12 produced by a transmission electron microscope in a process that is commonly referred to as transmission electron microscopy (TEM). As is readily seen in FIG. 4, each individual particle of the nano-particle material 12 comprises a generally cylindrically shaped, rod-like configuration having a mean length that is greater than its mean diameter. While the size of the nano-particle material 12 can be expressed in terms of the mean length or the mean diameter of the particles (e.g., as detected by transmission electron microscopy), it is generally more useful to express the size of the nano-particle material 12 in terms of surface area per unit weight due to the correlation between size and surface area. Measurements of particle surface area per unit weight may be obtained by BET analysis which is, as mentioned above, an established analytical technique that provides highly accurate and definitive results. In the embodiment shown and described herein, the method and apparatus of the present invention has been used to produce a nano-particle material having a size in the range of about 4-44 square meters/gram (m²/g) (15-35 m²/g preferred) as measured in accordance with the BET analysis technique. Alternatively, other types of measuring processes may be used to determine the particle size.

EXAMPLE 1

In this Example 1, the precursor material comprised a “technical grade” molybdic oxide (MoO₃) powder having a typical size of about 24-260 microns. Such technical grade molybdic oxide powder is produced by the Climax Molybdenum Company of Fort Madison, Iowa, and is readily commercially available therefrom. The precursor material was provided to an electrically heated sublimation furnace of the type described above having a capacity to sublimate or vaporize approximately 284 kg/hr of precursor material. In this Example 1, the capacity of the sublimation furnace is considerably greater than was required to produce the amount nano-particle material 12 described in this Example. This is because the sublimation furnace is used in a conventional manner to produce a highly purified sublimed MoO₃ material in accordance with a conventional process. The conventionally produced sublimed MoO₃ material comprises particles that are much larger than the nano-sized particles produced according to the present invention. Therefore, most of the sublimed or vaporized MoO₃ produced by the furnace was used in the conventional process, with only a small portion being drawn-off through the precipitation conduit to produce the nano-particle material in accordance with the method and apparatus of the present invention.

A precipitation conduit having the configuration and dimensions of the precipitation conduit described above was mounted within the vapor region contained within the sublimation furnace. The precipitation conduit was connected to a collection manifold which was connected to a product collection apparatus. The inlet end of the quench fluid tube was connected to a supply of quench fluid (e.g., liquid nitrogen) in accordance with the description provided herein. The technical grade MoO₃ precursor material was fed into the sublimation furnace in a continuous manner by a screw type conveyer system. Once within the furnace, the MoO₃ precursor material was heated to a temperature of about 1100° C. which was sufficient to sublime the MoO₃ precursor material. The pump associated with the product collection apparatus was then turned on. As mentioned above, the pump has a capacity of about 2831 liters/minute. Liquid nitrogen was utilized as the quenching fluid and was introduced into the inlet end of the quench fluid tube at a pressure of about 1.3 bar. An accumulator was used to ensure that the nitrogen entered the quench fluid tube as a liquid. Once the nitrogen flow was initiated, the apparatus started to produce the nano-particle material, which was thereafter captured by the filter assembly associated with the product collection apparatus. The flow-rate of the liquid nitrogen quench fluid was such that the temperature of the carrier stream containing the nano-particle product 12 as measured by the thermocouple positioned within the precipitation conduit 20 was maintained in the range of about 37°-54° C. The apparatus was operated in this manner for a time period of about 120 minutes, which resulted in the production of about 2.26 kg of nano-particle material.

Another embodiment of the invention 110 is shown in FIG. 5. The second embodiment 110 is similar to the first embodiment 10 described above, but includes additional elements, alternative configurations, and process steps that allow the second embodiment 110 to be used advantageously to produce nano-particles 112 having generally larger BET numbers.

With reference now primarily to FIG. 5, the second embodiment 110 of apparatus for producing nano-particles is shown and described herein as it may be used to produce nano-particles 112 of molybdenum oxide (MoO₃) from a precursor material 114. Of course, and as was the case for the first embodiment 10 already described, the second embodiment 110 also may be used to produce nano-particles of other vaporizable or sublimable materials, as would be obvious to persons having ordinary skill in the art after having become familiar with the teachings of the present invention.

The apparatus 110 for producing nano-particles 112 may comprise a sublimation furnace 116. In the embodiment shown and described herein, the sublimation furnace 116 may be substantially identical to the sublimation furnace 16 described above for the first embodiment and may be define at least one vapor region 118. A precipitation conduit 120 having an inlet end 122 and an outlet end 124 extends into the vapor region 118 so that the inlet end 122 of precipitation conduit 120 is exposed to vaporized (e.g., sublimated) material 136 contained within the vapor region 118 of furnace 116. The outlet end 124 of precipitation conduit 120 is connected to a product collection apparatus 126 which collects the nano-particle product 112. In one embodiment, the precipitation conduit 120 is also provided with a service opening 123 to allow convenient access to an interior region 129 defined by the precipitation conduit 120. The service opening 123 may be closed by a suitable removable fitting, such as an OPW-type fitting 157.

The inlet end 122 of precipitation conduit 120 defines an isolation chamber 128 within which is provided a quench fluid port 130. The quench fluid port 130 is fluidically connected a quench fluid supply apparatus 190, which supplies a quench fluid 132 in a gas state and a quench fluid in a liquid state, as will be described in greater detail below. After the quench fluid 132 in the gas and liquid states are combined, the quench fluid 132 is discharged by the quench fluid port 130 as a quench fluid stream 134. As was already described for the first embodiment 10, the quench fluid stream 134 of the second embodiment 110 rapidly cools the vaporized material 136 flowing through the precipitation conduit 120, resulting in the precipitation of the nano-particle material 112. The precipitated nano-particle material 112 continues to be carried along the precipitation conduit 120 to the product collection apparatus 126.

The precipitation conduit 120 may comprise a generally elongate, pipe-like member 146 that defines the inlet end 122, the outlet end 124, and the service opening 123 of precipitation conduit 120. However, unlike the precipitation conduit 20 for the first embodiment 10, the precipitation conduit 120 of the second embodiment 110 is not provided with an outer pipe-like member (e.g., member 48).

The pipe-like member 146 comprising precipitation conduit 120 may have dimensions that are commensurate with the size (i.e., desired production capacity) of the apparatus 110 for producing nano-particles. In the embodiment shown and described herein, the pipe-like member 146 has an inside diameter of about 76.2 mm, a wall thickness of about 7.6 mm and a length of about 1524 mm. Approximately 609.6 mm of the inlet end 122 of the pipe-like member 146 extends into the furnace 116.

The pipe-like member 146 comprising precipitation conduit 120 may be fabricated from any of a wide variety of materials (e.g., high-temperature alloys and stainless steels) suitable for the intended application. By way of example, in one preferred embodiment, the pipe-like member 146 is fabricated from high-temperature steel (e.g., type RA300) since the inlet end 122 of pipe-like member 146 is exposed to the high temperatures in the vapor region 118 of sublimation furnace 116.

The precipitation conduit 120 is provided with the quench fluid port 130 suitable for discharging the quench fluid stream 134 into the pipe-like member 146 comprising precipitation conduit 120. In the embodiment shown and described herein, the quench fluid port 130 may comprise an elongate tube-like member or quench fluid tube 154 having a branched inlet end 156 and a J-shaped outlet end 158. The branched inlet end 156 is fluidically connected to the quench fluid supply apparatus 190 and receives the quench fluid 132 in both the gas state and the liquid state in the manner that will be described in greater detail below. The J-shaped outlet end 158 of quench fluid tube defines the quench fluid port 130 and is positioned within the isolation chamber 128 so that the quench fluid port 130 is directed toward the downstream or outlet end 124 of precipitation conduit 120. Consequently, the quench fluid stream 134 discharged by the quench fluid port 130 is directed generally toward the outlet end 124 of precipitation conduit 120.

As mentioned above, the branched inlet end 156 of quench fluid tube 154 is fluidically connected to the quench fluid supply apparatus 190. More specifically, in the embodiment shown and described herein, a gas quench fluid inlet portion 184 of branched inlet end 156 is fluidically connected to a first supply 200 of quench fluid 132 in the gas state, whereas a liquid quench fluid inlet portion 186 of branched inlet end 156 is connected to a second supply 202 of quench fluid 132 in the liquid state. In the embodiment shown and described herein, the first supply 200 of quench fluid 132 in the gas state and the second supply 202 of quench fluid 132 in the liquid state 202 are contained with an accumulator 162 that is fluidically connected to a supply of quench fluid 132. Accumulator 162 functions as a separator, separating the quench fluid 132 into a gas-state portion (e.g., first supply 200) and a liquid-state portion (e.g., second supply 202). The gas-state portion (e.g., supply 200) and the liquid state portion (e.g., supply 202) are separated in accumulator 162 by a gas/liquid interface 135. Accordingly, accumulator 162 ensures that the quench fluid 132 is delivered to the branched inlet 156 of quench fluid tube 154 in both the gas state and the liquid state. Alternatively, of course, other arrangements may be used to provide to the branched inlet end 156 of quench fluid tube 154 the quench fluid 132 in both the gas and liquid states, as would be obvious to persons having ordinary skill in the art after having become familiar with the teachings of the present invention.

A first valve 139 is connected between the first supply 200 of quench fluid 132 in the gas state and the gas quench fluid inlet portion 184 of branched inlet 156. A second valve 137 is connected between the second supply 202 of quench fluid 132 in the liquid state and the liquid quench fluid inlet portion 186 of branched inlet 156. A valve control system 220 operatively connected to the first and second valves 139 and 137 may be used to operate or control the positions of the first and second valves 139 and 137 in a manner to be described in greater detail below.

The apparatus 110 is also provided with a temperature sensor or thermocouple 155 provided within the interior region 129 of precipitation conduit 120. The temperature sensor or thermocouple 155 senses the temperature of the carrier stream containing the nano-particle product 112 and produces an output signal 171 related thereto. In the embodiment shown and described herein, the distal end 153 of the thermocouple 155 is highly responsive to temperature changes and is located at a position about 914 mm downstream of the quench fluid port 130. Therefore, the temperature sensed by the thermocouple 155 corresponds to the temperature of the carrier stream containing the nano-particle product 112 at about that location.

The temperature sensor or thermocouple 155 is operatively connected to the valve control system 220 so that the valve control system 220 receives the output signal 171 from the temperature sensor 155. The valve control system 220 utilizes the output signal 171 from temperature sensor 155 to operate the valve 137 in order to control the temperature in the precipitation conduit 120, or, more precisely, the temperature of the carrier stream containing the nano-particle product 112 that flows over the distal end 153 of temperature sensor 155. In the embodiment 110 shown and described herein, a desired range temperature range for the carrier stream and suspended nano-particle material 112 is in the range of about 32.3°-54.4° C. (48° C. preferred).

The apparatus 110 is also provided with a pressure sensor 159 that is operatively associated with the branched inlet end 156 of the quench fluid tube 154. The pressure sensor 159 senses the pressure of the quench fluid 132 contained in the branched inlet end 156 of the quench fluid tube 154 and produces an output signal 173 related thereto. The pressure sensor 159 is operatively connected to the valve control system 220 so that the valve control system 220 receives the output signal 173 from the pressure sensor 159. The valve control system 220 utilizes the output signal 173 from pressure sensor 159 to operate the first valve 139 in order to control the pressure of the quench fluid 132 contained in the branched inlet end 156 of quench fluid tube 154. In the embodiment shown and described herein, a desired pressure range for the quench fluid 132 contained in the branched inlet end 156 of quench fluid tube 154 is in the range of about of 2-5 bar.

The location of the quench fluid port 130 within the precipitation conduit 120 has some influence on the sizes of the nano-particles 112 produced by the apparatus 110 according to the present invention. For example, moving the location of the fluid port 130 closer to the inlet end 122 of precipitation conduit 120 generally results in larger nano-particles 112 being produced. Conversely, moving the location of the fluid port 130 away from the inlet end 122 generally results in smaller nano-particles 112. However, other factors can also affect the particle size. For example, locating the heating elements (e.g., heating elements 50, FIG. 1) of the furnace (e.g., 116) within close proximity to precipitation conduit 120 and thereby subjecting precipitation conduit 120 to greater radiant energy tends to result in the production of smaller nano-particles 112 with larger BET numbers. In addition, smaller nano-particles can be produced even when the fluid port 130 is positioned closer to the inlet end 122 of precipitation conduit 120 by increasing the flow rate of the product collection device 126. That is, higher flow rates (e.g., liters/minute) will result in a higher velocity flow within the precipitation conduit 120. Of course, the velocity within the precipitation conduit 120 can also be changed by varying the inside diameter of the precipitation conduit 120.

Since the sizes of the nano-particles produced by the apparatus of the present invention are related to several structural and operational parameters of the invention, as described herein, the present invention should not be regarded as limited to any particular parameters or range of parameters for any given structural or operational configuration. However, by way of example, in one preferred embodiment, the quench fluid port 130 is positioned within the precipitation conduit 120 so that quench fluid port 130 is located about 300 mm from the inlet end 122 of precipitation conduit 120. This position of the quench fluid port 130, combined with the other parameters specified herein, will result in the formation of a nano-particle product substantially as described herein.

As mentioned above, the apparatus 110 is also provided with a collection manifold 144. Collection manifold 144 serves as a convenient means for directing the nano-particles 112 into the product collection system 126. In the embodiment illustrated in FIG. 5, the collection manifold 144 defines an interior chamber 164 having an outlet end 166 that is connected to the production collection system 126. The collection manifold 144 may be fabricated from any of a wide range of materials suitable for the intended application, as would be obvious to persons having ordinary skill in the art after having become familiar with the teachings of the present invention. By way of example, in one preferred embodiment, the collection manifold 144 is fabricated form type SAE 316 stainless steel, although other mild steel alloys, ceramics, or other suitable materials may also be used.

The product collection system 126 may comprise a blower or pump 142 and filter assembly 140. The blower or pump 142 draws a vaporized precursor material 136 through the precipitation conduit 120, the collection manifold 144 and filter assembly 140. More precisely, the vaporized material 136 is converted within the precipitation conduit 120 into a carrier stream having the nano-particle material 112 suspended therein. The carrier stream containing the suspended nano-particle material 112 continues to be drawn through the precipitation conduit 120 under the action of pump 142, ultimately reaching the filter assembly 140. The filter assembly 140 removes the nano-particle material 112 from the carrier stream. The carrier stream is then discharged into the surrounding atmosphere as a filtered carrier stream 168. The filter assembly 140 may be harvested from time to time to remove the captured nano-particle material 112.

The blower or pump 142 utilized in the product collection system 126 may comprise any of a wide range of air pump devices that are well-known in the art and readily commercially available. By way of example, in one preferred embodiment, the pump 142 comprises a centrifugal blower having a capacity of about 8400 (e.g., 8495) liters per minute. Alternatively, the pump 142 may have either a larger or smaller capacity depending on the intended production capacity of the nano-particle production apparatus 110. In another embodiment, the pump 142 may be provided with a variable capacity to allow the user to vary the flow rate of the pump 142 to more easily effect certain changes in the sizes of the nano-particle material 112.

The filter assembly 140 may comprise any of a wide range devices suitable for removing small particles from an air stream. By way of example, in the embodiment shown and described herein, the filter assembly 140 comprises a particulate filter medium fabricated from Gore-Tex®. The filter material should be sufficiently fine so that it will capture substantially all of the nano-particle material 112 exiting the collection manifold 144. However, since filters for capturing such nano-sized particles are well-known in the art and could be easily provided by persons having ordinary skill in the art after having become familiar with the teachings of the present invention, the filter utilized in one preferred embodiment of the present invention will not be described in further detail herein.

In an alternative arrangement, the filter assembly 140 may comprise a liquid scrubber-type filter wherein the nano-particle material 112 is collected by bubbling the carrier stream and nano-particle material 112 through a liquid (e.g., alcohol), although other liquids may be used. The liquid captures the nano-particle material which may thereafter be removed from the liquid by conventional techniques. Still other filtering devices and processes are possible and could be used to capture and remove the nano-particle product 112 from the carrier stream, as would be obvious to persons having ordinary skill in the art after having become familiar with the teachings of the present invention. Consequently, the present invention should not be regarded as limited to the particular product collection apparatus shown and described herein.

The apparatus 110 may be operated in accordance with the following method in order to produce nano-particles 112 of MoO₃. The precursor material 114 may be fed into the sublimation furnace 116 in either a continuous manner or in batches. In the embodiment shown and described herein, the precursor material 114 is fed into the furnace 116 in a continuous manner by a screw-type conveyer system (e.g., conveyer system 60, FIG. 1). Once the precursor material 114 is delivered to the sublimation furnace 116, the sublimation furnace 116 heats the precursor material 114 to a temperature of at least about 800° C. (with optimum results being obtained within a temperature range of about 1093°-1260° C.), which is sufficient to sublime the MoO₃ precursor material 114, resulting in the product of a vaporized or sublimed precursor material 136. Sublimation of the precursor material 114 allows the production of a highly purified nano-particle product 112.

The sublimed or vaporized precursor material 136 may be combined with a carrier gas 138, such as air or any other desired atmosphere, to assist in the flow of the vaporized or sublimed precursor material 136 into the inlet end 122 of the precipitation conduit 120. Upon being drawn into the inlet end 122 of precipitation conduit 120, the vaporized precursor material 136 enters isolation chamber 128. Isolation chamber 128 isolates the vaporized precursor material 136 from region 118. As the vaporized precursor material 136 continues to travel down the precipitation conduit 120, it eventually contacts the quench fluid stream 134 being discharged by the quench fluid port 130 provided on the J-shaped outlet end 158 of quench fluid tube 154. The quench fluid stream 134 being discharged by the fluid port 130 is considerably cooler than the vaporized precursor material 136. This results in the rapid (i.e., substantially adiabatic) cooling of the vaporized precursor material 136. The rapid cooling results in the precipitation of the nano-particle product 112 form the vaporized precursor material 136. The resulting mixture of precipitate (in the form of the nano-particle product 112) and carrier stream (e.g., air or inert or other gas atmosphere) continues to be carried down the precipitation conduit 120, whereupon it is discharged into the collection manifold 144. Thereafter, the nano-particle product 112 is ultimately captured by the filter 140 of the production collection system 126. The remaining carrier stream passes through the pump 142 and is discharged into the surrounding atmosphere as filtered carrier stream 168.

As mentioned above, the quench fluid stream 134 discharged by the quench fluid port 130 is formed by mixing quench fluid 132 in a gas state (e.g., from the first supply 200) and quench fluid 132 in a liquid state (e.g., from the second supply 202) at the branched inlet end 156 of quench fluid tube 154. In addition, the valve control system 220 operates the valves 139 and 137 in order to control the temperature of the carrier stream containing the nano-particle product 112 and the pressure of the quench fluid 132 entering the branched inlet end 156 of quench fluid tube 154. More specifically, the amount of quench fluid 132 in the liquid state (e.g., from second supply 202) that is allowed to enter the branched inlet end 156 of quench fluid tube 154 affects the temperature of the carrier stream containing the nano-particle product 112 flowing in the precipitation conduit 120. Accordingly, the valve control system 220 utilizes the output signal 171 from the temperature sensor 155 to control the position of valve 137, thereby varying the amount of quench fluid 132 in the liquid state entering branched inlet end 156 of quench fluid tube 154. Generally speaking, larger amounts of quench fluid 132 in the liquid state will result in lower temperatures of the carrier stream containing the nano-particle material 112, whereas smaller amounts of quench fluid 132 in the liquid state will result in higher temperatures of the carrier stream containing the nano-particle material 112. The control system 220 operates the valve 137 as necessary to maintain the temperature of the carrier stream containing the nano-particle material 112 within the range specified herein.

The pressure of the quench fluid 132 in the branched inlet end 156 of quench fluid tube 154 is controlled by varying the amount of quench fluid 132 in the gas state (e.g., from supply 200) that is allowed to enter the branched inlet end 156. The valve control system 220 utilizes the output signal 173 from the pressure sensor 159 to control the position of valve 139, thereby varying the amount of quench fluid 132 in the gas state entering the branched inlet end 156 of quench fluid tube 154. Generally speaking, larger amounts of quench fluid 132 in the gas state will result in higher pressures, whereas smaller amounts of quench fluid 132 in the gas state will result in lower pressures. The control system 220 operates the valve 139 as necessary to maintain the pressure of the quench fluid 132 in the branched inlet end 156 of quench fluid tube 154 within the range specified herein. In this regard, it should be noted that the pressure of the quench fluid 132 in the branched inlet end 156 is also affected to some degree by the amount of quench fluid 132 in the liquid state that is allowed to enter the branched inlet end 156. That is, the operation of valve 137 will also affect the pressure of the quench fluid 132 in the branched inlet end 156. However, primary control of the pressure of the quench fluid 132 in the branched inlet end 156 is accomplished by controlling valve 139.

FIG. 6 is an image produced by a transmission electron microscope of the nano-particle material 112 produced by apparatus 110 shown and described herein. The method and apparatus of the present invention has been used to produce a nano-particle material having a size in the range of about 15-68 square meters/gram (m²/g) (55 m²/g preferred) as measured in accordance with the BET analysis technique. Alternatively, other types of measuring processes may be used to determine the particle size.

EXAMPLE 2

In this Example 2, the precursor material 114 comprised a “technical grade” molybdic oxide (MoO₃) powder having a typical size of about 24-260 microns. Such technical grade molybdic oxide powder is produced by the Climax Molybdenum Company of Fort Madison, Iowa, and is readily commercially available therefrom. The precursor material 114 was provided to an electrically heated sublimation furnace (e.g., 116) of the type described above having a capacity to sublimate or vaporize approximately 284 kg/hr of precursor material. It should be noted that the capacity of the sublimation furnace is considerably greater than was required to produce the amount nano-particle material 112 described in this Example 2. This is because the sublimation furnace is used in a conventional manner to produce a highly purified sublimed MoO₃ material in accordance with a conventional process. The conventionally produced sublimed MoO₃ material comprises particles that are much larger than the nano-sized particles produced according to the present invention. Therefore, most of the sublimed or vaporized MoO₃ produced by the furnace was used in the conventional process, with only a small portion being drawn-off through the precipitation conduit 120 to produce the nano-particle material in accordance with the method and apparatus of the present invention.

A precipitation conduit having the configuration and dimensions of the precipitation conduit 120 shown in FIG. 5 and described herein was mounted within the vapor region contained within the sublimation furnace. The precipitation conduit was connected to a collection manifold which was connected to a product collection apparatus. The technical grade MoO₃ precursor material was fed into the sublimation furnace in a continuous manner by a screw type conveyer system. Once within the furnace, the MoO₃ precursor material was heated to a temperature of about 1100° C. which was sufficient to sublime the MoO₃ precursor material. The pump associated with the product collection apparatus was then turned on. As mentioned above, the pump has a capacity of about 8495 liters/minute. The branched inlet end of the quench fluid tube was connected to a quench fluid supply apparatus 190 which supplied nitrogen quench fluid 132 in a gas state and in a liquid state in accordance with the description provided herein. The valve control system 220 was used to maintain the pressure of the quench fluid 132 in the branched inlet end 156 at about 4.13 bar. Once the combined liquid and gaseous nitrogen flow was initiated, the apparatus started to produce the nano-particle material, which was thereafter captured by the filter assembly associated with the product collection apparatus. The valve control system 220 was used to maintain the temperature of the carrier stream containing the nano-particle product 112 at about 48° C. The apparatus was operated in this manner for a time period of about 480 minutes, which resulted in the production of about 29 kg of nano-particle material.

It is readily apparent that the apparatus and process discussed herein may be used to produce large quantities of MoO₃ nano-particle material with much simpler apparatus and without being overly sensitive to certain process control parameters. Consequently, the claimed invention represents an important development in nano-particle technology in general and to molybdenum nano-particle technology in particular. Having herein set forth preferred embodiments of the present invention, it is anticipated that suitable modifications can be made thereto which will nonetheless remain within the scope of the present invention. Therefore, it is intended that the appended claims be construed to include alternative embodiments of the invention except insofar as limited by the prior art. 

1. A method for producing nano-particles from a precursor material, comprising: vaporizing the precursor material to produce a vapor; directing the vapor into an isolation chamber; combining a quench fluid in a gaseous state with a quench fluid in a liquid state to form a quench fluid stream; contacting the vapor contained in the isolation chamber with the quench fluid stream, the quench fluid stream cooling the vapor to produce the nano-particles in a carrier stream; and removing the nano-particles from the isolation chamber.
 2. The method of claim 1, further comprising varying a temperature of the carrier stream by varying an amount of quench fluid in the liquid state that is used to form the quench fluid stream.
 3. The method of claim 2, further comprising: sensing a temperature of the carrier stream; and varying the amount of quench fluid in the liquid state that is used to form the quench fluid stream based on the sensed temperature of the carrier stream.
 4. The method of claim 2, wherein the temperature of the carrier stream is varied in the range of about 32.3°-54.4° C.
 5. The method of claim 1, further comprising varying a pressure of the quench fluid stream by varying an amount of quench fluid in the gaseous state that is used to form the quench fluid stream.
 6. The method of claim 5, further comprising: sensing a pressure of the quench fluid stream; and varying the amount of quench fluid in the gaseous state that is used to form the quench fluid stream based on the sensed pressure.
 7. The method of claim 5, wherein the pressure in the downstream interior region is varied within the range of about 2 to 5 bar.
 8. The method of claim 1, wherein the precursor material comprises MoO₃.
 9. The method of claim 8, wherein the sublimating the MoO₃ precursor material takes place at a temperature in the range of about 1093°-1260° C.
 10. The method of claim 1, wherein the quench fluid is cryogenic fluid.
 11. The method for producing nano-particles, comprising: providing a supply of precursor material; providing a single source of quench fluid, the quench fluid being in a gaseous state and a liquid state; sublimating the precursor material to produce a vapor; directing the vapor into a precipitation conduit; drawing off quench fluid in the gaseous state from the single source; drawing off quench fluid in the liquid state from the single source; mixing quench fluid in the gaseous state and quench fluid in the liquid state to form a quench fluid stream; causing precipitation of the nano-particles in the precipitation conduit by contacting the vapor with the quench fluid stream; and collecting the nano-particles.
 12. The method of claim 11 further comprising directing the nano-particles into a product collection apparatus.
 13. The method of claim 11 wherein the quench fluid is cryogenic fluid.
 14. The method of claim 11 wherein the single source comprises a gas-liquid interface and wherein the drawing off of quench fluid in the gaseous state occurs above the gas-liquid interface and the drawing off of quench fluid in the liquid state occurs below the gas-liquid interface.
 15. A method for producing nano-particles, comprising: providing a supply of precursor material; providing a supply of quench fluid; separating the supply of quench fluid into a first quench fluid supply and a second quench fluid supply, the first quench fluid supply and the second quench fluid supply consisting essentially of the same substance, the first quench fluid supply being the quench fluid in the gaseous state and the second quench fluid supply being the quench fluid in the liquid state; sublimating the precursor material to produce vapor; directing the vapor into an isolation chamber; creating a quench fluid stream by withdrawing quench fluid in the gaseous state from the first quench fluid supply, withdrawing quench fluid in the liquid state from the second quench fluid supply and combining the quench fluid in the gaseous state with the quench fluid in the liquid state; directing the quench fluid stream into the isolation chamber; contacting the vapor in the isolation chamber with the quench fluid stream, producing nano-particles; and removing the nano-particles from the isolation chamber.
 16. The method of claim 15 wherein the separating comprises placing the first quench fluid supply and the second quench fluid supply in a single vessel.
 17. The method of claim 16 further comprising maintaining a separation between the first quench fluid supply and the second quench fluid supply with a liquid-gas interface. 